Paints
are basically a type of adhesive. Chlorinated paint is made of neoprene
(Poly chloroprene Neoprene or poly-chloroprene), is the basis for one of
the largest and most important groups of rubber adhesives. At present
27 neoprene are produced in solid form, and 16 in latex form; most of
them have been used in adhesives.
The rapid development of bond strength of films from solution, combined with tack or auto adhesion, as well as resistance of the cured glue line to heat oxidation, water, solvents, oils, acid and alkalis, have led to the extensive use of neoprene solvent cements in the shoe, furniture, automotive, paint and construction industries.
Preparation of modified chlorinated rubber paint using “GRAPHITE” precedes by the following method:- Graphite added to xylene and stirring the mixture.Adding chlorinated rubber dissolved in xylene, toluene and butyl acetate solution.Finally in this dispersion chlorinated paraffins and phenloic resins are added undergoing mixing, shearing and filtering to obtain a paint.
Our project involves three different formulation of chlorinated rubber paint where a pre-modified graphite is used in manufacturing chlorinated rubber paint.The pre-modified graphite adds on to the poor thermal stability of chlorinated rubber.Natural graphite has a good thermal stability and flame retardancy .
Adding a certain amount of graphite, would significantly improve its thermal stability.The present invention is prepared using graphite oxide its carbon content is 60-84%, oxygen content is 15-38%. Thus we are aiming to carry out this project at L.D. College of the Engineering Ahmedabad for improving the properties at comparatively.
The rapid development of bond strength of films from solution, combined with tack or auto adhesion, as well as resistance of the cured glue line to heat oxidation, water, solvents, oils, acid and alkalis, have led to the extensive use of neoprene solvent cements in the shoe, furniture, automotive, paint and construction industries.
Preparation of modified chlorinated rubber paint using “GRAPHITE” precedes by the following method:- Graphite added to xylene and stirring the mixture.Adding chlorinated rubber dissolved in xylene, toluene and butyl acetate solution.Finally in this dispersion chlorinated paraffins and phenloic resins are added undergoing mixing, shearing and filtering to obtain a paint.
Our project involves three different formulation of chlorinated rubber paint where a pre-modified graphite is used in manufacturing chlorinated rubber paint.The pre-modified graphite adds on to the poor thermal stability of chlorinated rubber.Natural graphite has a good thermal stability and flame retardancy .
Adding a certain amount of graphite, would significantly improve its thermal stability.The present invention is prepared using graphite oxide its carbon content is 60-84%, oxygen content is 15-38%. Thus we are aiming to carry out this project at L.D. College of the Engineering Ahmedabad for improving the properties at comparatively.